<*n class="catname"><*n>物理性能*n>*n> |
<*n>额定值*n>
|
<*n>单位制*n>
|
<*n>测试方法*n>
|
<*n><*n>比重<*n class="context">*n>*n>*n>
|
<*n>1.20*n>
|
<*n>g/cm³*n>
|
<*n class="standard"><*n>ASTM D792*n>*n> |
<*n><*n>熔流率(熔体流动速率)<*n class="context"><*n class="Apple-converted-*ce"> *n>(300°C/1.2
kg)*n>*n>*n>
|
<*n>10*n>
|
<*n>g/10 min*n>
|
<*n class="standard"><*n>ASTM D1238*n>*n> |
<*n><*n>收缩率 - 流动<*n class="Apple-converted-*ce"> *n><*n class="context">(3.20 mm)*n>*n>*n>
|
<*n>0.50 到 0.70*n>
|
<*n>%*n>
|
<*n class="standard"><*n>ASTM D955*n>*n> |
<*n class="catname"><*n>硬度*n>*n> |
<*n>额定值*n>
|
<*n>单位制*n>
|
<*n>测试方法*n>
|
<*n><*n>洛氏硬度<*n class="context"><*n class="Apple-converted-*ce"> *n>(R 级, 23°C)*n>*n>*n>
|
<*n>122*n>
|
<*n>*n>
|
<*n class="standard"><*n>ASTM D785*n>*n> |
<*n class="catname"><*n>机械性能*n>*n> |
<*n>额定值*n>
|
<*n>单位制*n>
|
<*n>测试方法*n>
|
<*n><*n>*张强度<*n style="font-size:12px;vertical-align:baseline;line-height:0;"> <*n class="PROPERTY">3*n>*n><*n class="context"><*n class="Apple-converted-*ce"> *n>(屈服)*n>*n>*n>
|
<*n>61.8*n>
|
<*n>MPa*n>
|
<*n class="standard"><*n>ASTM D638*n>*n> |
<*n><*n>伸长率<*n style="font-size:12px;vertical-align:baseline;line-height:0;"> <*n class="PROPERTY">3*n>*n><*n class="context"><*n class="Apple-converted-*ce"> *n>(断裂)*n>*n>*n>
|
<*n>100*n>
|
<*n>%*n>
|
<*n class="standard"><*n>ASTM D638*n>*n> |
<*n><*n>弯曲模量<*n style="font-size:12px;vertical-align:baseline;line-height:0;"> <*n class="PROPERTY">4*n>*n><*n class="context">*n>*n>*n>
|
<*n>2350*n>
|
<*n>MPa*n>
|
<*n class="standard"><*n>ASTM D790*n>*n> |
<*n><*n>弯曲强度<*n style="font-size:12px;vertical-align:baseline;line-height:0;"> <*n class="PROPERTY">4*n>*n><*n class="context">*n>*n>*n>
|
<*n>90.2*n>
|
<*n>MPa*n>
|
<*n class="standard"><*n>ASTM D790*n>*n> |
<*n class="catname"><*n>冲击性能*n>*n> |
<*n>额定值*n>
|
<*n>单位制*n>
|
<*n>测试方法*n>
|
<*n><*n>悬壁梁缺口冲击强度<*n class="context"><*n class="Apple-converted-*ce"> *n>(23°C, 0.125
mm)*n>*n>*n>
|
<*n>780*n>
|
<*n>J/m*n>
|
<*n class="standard"><*n>ASTM D256*n>*n> |
<*n class="catname"><*n>热性能*n>*n> |
<*n>额定值*n>
|
<*n>单位制*n>
|
<*n>测试方法*n>
|
<*n><*n>载荷下热变形温度<*n style="font-size:12px;vertical-align:baseline;line-height:0;"> <*n class="PROPERTY">5*n>*n><*n class="context"><*n class="Apple-converted-*ce"> *n>(1.8 MPa,
未退火)*n>*n>*n>
|
<*n>125*n>
|
<*n>°C*n>
|
<*n class="standard"><*n>ASTM D648*n>*n> |
<*n><*n>维卡软化温度<*n class="context">*n>*n>*n>
|
<*n>143*n>
|
<*n>°C*n>
|
<*n class="standard"><*n><*n>ASTM D1525<*n style="font-size:12px;vertical-align:baseline;line-height:0;"> <*n class="STANDARD">6*n>*n>*n>*n>*n> |
<*n class="catname"><*n>可燃性*n>*n> |
<*n>额定值*n>
|
<*n>*n>
|
<*n>测试方法*n>
|
<*n><*n>UL 阻燃等级<*n class="context"><*n class="Apple-converted-*ce"> *n>(1.10 mm)*n>*n>*n>
|
<*n>V-0*n>
|
<*n>*n>
|
<*n class="standard"><*n>UL 94*n>*n> |
<*n class="catname"><*n>注射*n>*n> |
<*n>额定值*n>
|
<*n>单位制*n>
|
<*n>*n>
|
<*n><*n>干燥温度<*n class="context">*n>*n>*n>
|
<*n>120*n>
|
<*n>°C*n>
|
<*n> *n> |
<*n><*n>干燥时间<*n class="context">*n>*n>*n>
|
<*n>4.0*n>
|
<*n>hr*n>
|
<*n> *n> |
<*n><*n>料筒后部温度<*n class="context">*n>*n>*n>
|
<*n>270 到 300*n>
|
<*n>°C*n>
|
<*n> *n> |
<*n><*n>料筒中部温度<*n class="context">*n>*n>*n>
|
<*n>270 到 300*n>
|
<*n>°C*n>
|
<*n> *n> |
<*n><*n>料筒前部温度<*n class="context">*n>*n>*n>
|
<*n>270 到 300*n>
|
<*n>°C*n>
|
<*n> *n> |
<*n><*n>模具温度<*n class="context">*n>*n>*n>
|
<*n>70.0 到 100*n>
|
<*n>°C*n>
|