ОПИСАНИЕМАГНЕЗИТОВОЙПЛИТЫ/
DESCRIPTI* OF GLASS MAGNESIUM BOARD
Glas*agnesium boa*- a modern, environmentally clean material for building and repair works. Basic advantages ofglas*agnesium boa*are their incombustibility and moisture resistance, that can be used in buildings, to the c*tructi* of which are demanding heightened requirements for the fire safety or stability to influence of atmospheric environment. Excellent heat- and sound-proof properties allow to useglas*agnesium boa*practically for any kinds of repair and building works. Main com*ition ofglas*agnesium board: Magnesium oxide : 40.7% Magnesium chloride: 33.7% Pearlite: 11.6% Wood-fibre: 11.6% Fiberglass/ Nonwoven：2.4% Density: 0.95g/cm3 | Магнезитовые плиты- современный экологически чистый материал для строительных и ремонтных работ. Основными преимуществами магнезитовых плит являются их несгораемость и влагостойкость, что может быть использовано в сооружениях, к конструкциям которых предъявляются повышенные требования по пожарной безопасности или устойчивости к воздействию окружающей атмосферной среды. Отличные тепло- и звукоизоляционные свойства позволяют использовать магнезитовые плиты практически для любых видов ремонтных и строительных работ. Основной состав магнезитовой плиты: Окись магния: 40.7% Хлористый магний: 33.7% Перлит: 11.6% Древесное волокно: 11.6% Стекловолокно/Нетканные материалы：2.4% Плотность: 0.95g/cm3 |
QUALITY CERTIFICATE
PRODUCT NAME: GLASS MAGNESIUM BOARD
SIZE: 8.0mm*1220mm*2440mm
STANDA*B/T 7019-1997, JC688-2006, GB/T 10294-2008,GB/T 9775-2008
DATE OF ISSUE: 2011-05-30
ITEM | UNITS | RESULTS | |
1 | Shrinkage rate | % | 0.18 |
2 | Wet bilge rate | % | 0.51 |
3 | Hold screw force | N/mm | 34 |
4 | Density | g/cm3 | 0.95 |
5 | Water absorption | % | 34.7 |
6 | Water content | % | 16.2 |
7 | Bending load | N | 270 |
8 | Flexural strength | MPa | 10 |
9 | Boiling water resistance (Boiling water 2h) | No abnormalities Water absorption:12.2% Thickness rises: 2% | |
10 | Cold water dipping (20℃, 120h) | No abnormalities | |
11 | Warm water dipping (80℃, 6h) | No abnormalities | |
12 | PH value | 7.7 | |
13 | Anti-impact intensity | kJ/m2 | 2.1 |
14 | Impact resistance | Without radial crack on the back | |
15 | Coefficie*f thermal conductivity | W/(m·k) | 0.28(25℃,P:899kg/m3) |
16 | Chlorine ion content | % | 3.86 |
17 | Asbestos content | Non-asbestos |
Kunshan city fireproof material factory