登封市卢店镇开元磨料厂
钢包浇注料，****耐火浇注料，*浇注料
产品属性
钢包浇注料，****耐火浇注料，*浇注料
用途：主要用于循环流化床锅炉燃烧室、分离器及烟道等易冲刷磨损的部位。
|
项目 | 指标 | |||
NMJ-1 | NMJ-2 | NMJ-3 | ||
AL2O3 ％ | 60 | 65 | 70 | |
体积密度（g/cm3） | 110℃×24h干后 ≥ | 2.40 | 2.60 | 2.80 |
常温耐压强度 MPa | 110℃×24h干后 ≥ | 55 | 60 | 65 |
1000℃×3h烧后 ≥ | 80 | 90 | 100 | |
常温*折强度 MPa | 110℃×24h干后 ≥ | 7 | 8 | 9 |
1000℃×3h烧后 ≤ | 9 | 11 | 13 | |
烧后线变化 ％ | 1000℃×3h | -0.3~+0.3 | -0.3~+0.3 | -0.3~+0.3 |
常温磨损量 cm3 | 1000℃×3h烧后 ≤ | 9 | 8 | 7 |
*热震性 次 | （1000℃，水冷）≤ | 20 | 20 | 20 |
****使用温度 ℃ Max service tempeature | 1400 | 1450 | 1500 | |
Products- wearable castable series
Item | Products | SiC castables | Corundum castable | Ultra-high strength wear-resistant castable TNJ-150 | Steel fiber wearable castable | High-strength wear-resista*efractory castable TNJ-120 |
Al203% | ≥ | 88（SiC） | 85 | 82 | 80 | 80 |
Bulk Density g / cm3 | ≥ | 2.95 | * | 3.0 | 2.90 | 2.93 |
Compressive strength at common temperature | 110℃×24h | 120 | 160 | 150 | 125 | 120 |
MPa ≥ | 1000℃×3h | 135 | 190 | 180 | 140 | 130 |
Flexural strength at common temperature | 110℃×24h | 18 | 22 | 18 | 17 | 17 |
MPa ≥ | 1000℃×3h | 20 | 24 | 20 | 19 | 19 |
Line rate of change after burning | 1000℃×3h | -0.2~0.2 | -0.2~0.2 | -0.2~0.2 | -0.2~0.2 | -0.2~0.2 |
Thermal shock resistance | ≥1000℃ | 50 | 50 | 50 | 50 | 50 |
Wear at common temperature | ≤ | 2 | 2 | 3 | 3 | 4 |
The maximum temperature ℃ | ≥ | 1790 | 1790 | 1790 | 1790 | 1790 |
Item | Products | Wear-resistant castable TNJ-80 | Refractory castable TNJ-50 | Refractory concrete TNJ-30 |
Al203% | ≥ | 75 | 70 | 55 |
Bulk Density g / cm3 | ≥ | 2.75 | 2.65 | 2.2 |
Compressive strength at common temperature | 110℃×24h | 90 | 70 | 30 |
MPa ≥ | 1000℃×3h | 120 | 90 | 40 |
Flexural strength at common temperature | 110℃×24h | 14 | 12 | 5 |
MPa ≥ | 1000℃×3h | 16 | 14 | 7 |
Line rate of change after burning | 1000℃×3h | -0.2~0.2 | -0.2~0.2 | -0.3~0.3 |
Thermal shock resistance | ≥1000℃ | 50 | 30 | 20 |
Wear at common temperature | ≤ | 4 | 5 | —— |
The maximum temperature ℃ | ≥ | 1500 | 1450 | 1400 |
Induction Furnace Refractories Products
Indicators Project Grade | Al2O3+MgO+Cr2O3 % | Cr2O3 % | Al2O3 % | SiO2 % | CaO % | The maximum temperature | Uses | |
corundum material | ZP-B1 | 97.1 | 1760 | Suitable for large and medium-sized induction furnaces can be *elt containing nickel, chromium, and manganese, cobalt high-alloy steel and cast steel. | ||||
ZP-B2 | 96.6 | 1750 | ||||||
ZP-B3 | 96 | 1720 | ||||||
Repair material | ZP-K1 | 3.8 | 75.1 | 12.8 | 1760 | Supporting dry mouth and play materials for the furnace lining repair | ||
ZP-K2 | 90 | 4.3 | 1650 | Lining material used in the wet patch to play. | ||||
Spinel Ramming | MA-1 | 86.9 | 1650 | For cold-working die steel, ho*e steel, cast steel, etc. | ||||
MA-2 | 91.1 | 1700 | All structural steel used in high-speed tool steel, cast steel, etc. | |||||
MA-3 | 95 | 1710 | Can be used for refining stainless steel, military steel. | |||||
Siliceou*aterial | ZP-S | 97.2 | 1650 | Using acidic steel making, *elting carb*teel, low alloy steel, high silic*teel and ductile cast iron. | ||||
Magnesia Ramming | ZP-M1 | 91 | 1700 | For *all-capacity induction furnace, *eltin*ganese steel, high alloy steel. | ||||
ZP-M2 | 97 | 1850 | Vacuum induction furnace for *elting steel and high-temperature alloy precision. | |||||
Induction coil coating | ZP-T | 85.3 | 4.7 | 4.6 | Protective coating for the induction coil | |||