登封市卢店镇星光耐材磨料磨具厂

主营：地坪,人造磨料,天然磨料,石英,砂轮

Insulation refractory castable保温轻质浇注料

￥2900元/吨中国

产品属性

星光牌浇注料&*耐材浇注料!!浇注料价格%*耐火浇注料

水硬性结合浇注料在常温下凝结硬化并通过水化作用而硬化，主要品种有硅酸盐水泥、普通铝酸钙水泥、纯铝酸钙水泥、电熔纯铝酸钙水泥浇注料等。化学结合浇注料在常温下一般通过加入促硬剂形成化学反应而硬化，主要品种有水玻璃、*铝、****盐浇注料等。凝聚结合浇注料为在煅烧过程中经烧结作用而硬化，主要品种有粘土浇注料等。

Hydraulic combination castable in normal temperature condensation hardening and through hydration and hardening, themain varieties h*e silicate ceme*rdinary calcium aluminatecement, pure calcium aluminate cement, fused pure calcium aluminate cement castable, etc. Chemically bonded castable in normal temperature usually by join hardening agent form chemical reaction and hardening, the main varieties h*e water glass, aluminum sulfate, phosphate castable, etc. Coagulation combined with pouring material for sintering process in the nodulizing and hardening, the main varieties h*e clay pouring material, etc.

产品展示-*耐火浇注料系列

用途：主要用于循环流化床锅炉燃烧室、分离器及烟道等易冲刷磨损的部位。
产品主要理化指标

项目	产品	碳化硅浇注料	刚玉浇注料	超高强*耐火浇注料TNJ-150	钢纤维*耐火浇注料	高强*耐火浇注料TNJ-120
Al203%	≥	88(SiC)	85	82	80	80
体积密度 g/cm3	≥	2.95	*	3.0	2.90	2.93
常温耐压强度	110℃×24h	120	160	150	125	120
MPa≥	1000℃×3h	135	190	180	140	130
常温*折强度	110℃×24h	18	22	18	17	17
MPa≥	1000℃×3h	20	24	20	19	19
烧后线变化率 %	1000℃×3h	-0.2~0.2	-0.2~0.2	-0.2~0.2	-0.2~0.2	-0.2~0.2
热震稳定性次	1000℃水冷≥	50	50	50	50	50
常温磨损量 cm3	≤	2	2	3	3	4
****使用温度℃	≥	1790	1790	1790	1790	1790

项目	产品	*耐火浇注料TNJ-80	耐火浇注料TNJ-50	耐火混凝土TNJ-30
Al203%	≥	75	70	55
体积密度g/cm3	≥	2.75	2.65	2.2
常温耐压强度	110℃×24h	90	70	30
MPa≥	1000℃×3h	120	90	40
常温*折强度	110℃×24h	14	12	5
MPa≥	1000℃×3h	1 6	14	7
烧后线变化率%	1000℃×3h	-0.2~0.2	-0.2~0.2	-0.3~0.3
热震稳定性次	1000℃水冷≥	50	30	20
常温磨损量cm3	≤	4	5	________
****使用温度℃	≥	1500	1450	1400

项目 Item		指标 Indexes
项目 Item		NMJ-1	NMJ-2	NMJ-3
AL2O3　　％		60	65	70
体积密度（g/cm3） Bulk Density	110℃×24h干后 ≥	2.40	2.60	2.80
常温耐压强度 MPa Cold crushing strength	110℃×24h干后 ≥	55	60	65
常温耐压强度 MPa Cold crushing strength	1000℃×3h烧后 ≥	80	90	100
常温*折强度　MPa Modulus of rupture	110℃×24h干后 ≥	7	8	9
常温*折强度　MPa Modulus of rupture	1000℃×3h烧后 ≤	9	11	13
烧后线变化　％ Permanent Linear Change	1000℃×3h	-0.3~+0.3	-0.3~+0.3	-0.3~+0.3
常温磨损量　cm3	1000℃×3h烧后 ≤	9	8	7
*热震性　　次 Thermal shock resistance	（1000℃，水冷）≤	20	20	20
****使用温度　℃　Max service tempeature		1400	1450	1500

Products- wearable castable series

Item	Products	SiC castables	Corundum castable	Ultra-high strength wear-resistant castable TNJ-150	Steel fiber wearable castable	High-strength wear-resista*efractory castable TNJ-120
Al203%	≥	88（SiC）	85	82	80	80
Bulk Density g / cm3	≥	2.95	*	3.0	2.90	2.93
Compressive strength at common temperature	110℃×24h	120	160	150	125	120
MPa ≥	1000℃×3h	135	190	180	140	130
Flexural strength at common temperature	110℃×24h	18	22	18	17	17
MPa ≥	1000℃×3h	20	24	20	19	19
Line rate of change after burning	1000℃×3h	-0.2~0.2	-0.2~0.2	-0.2~0.2	-0.2~0.2	-0.2~0.2
Thermal shock resistance	≥1000℃	50	50	50	50	50
Wear at common temperature cm3cm3	≤	2	2	3	3	4
The maximum temperature ℃	≥	1790	1790	1790	1790	1790

Item	Products	Wear-resistant castable TNJ-80	Refractory castable TNJ-50	Refractory concrete TNJ-30
Al203%	≥	75	70	55
Bulk Density g / cm3	≥	2.75	2.65	2.2
Compressive strength at common temperature	110℃×24h	90	70	30
MPa ≥	1000℃×3h	120	90	40
Flexural strength at common temperature	110℃×24h	14	12	5
MPa ≥	1000℃×3h	16	14	7
Line rate of change after burning	1000℃×3h	-0.2~0.2	-0.2~0.2	-0.3~0.3
Thermal shock resistance	≥1000℃	50	30	20
Wear at common temperature cm3cm3	≤	4	5	——
The maximum temperature ℃	≥	1500	1450	1400

Induction Furnace Refractories Products

Indicators Project Grade		Al2O3+MgO+Cr2O3 %	Cr2O3 %	Al2O3 %	SiO2 %	CaO %	The maximum temperature	Uses
corundum material	ZP-B1	97.1					1760	Suitable for large and medium-sized induction furnaces can be *elt containing nickel, chromium, and manganese, cobalt high-alloy steel and cast steel.
	ZP-B2	96.6					1750
	ZP-B3	96					1720
Repair material	ZP-K1		3.8	75.1	12.8		1760	Supporting dry mouth and play materials for the furnace lining repair
Repair material	ZP-K2	90			4.3		1650	Lining material used in the wet patch to play.
Spinel Ramming	MA-1	86.9					1650	For cold-working die steel, ho*e steel, cast steel, etc.
	MA-2	91.1					1700	All structural steel used in high-speed tool steel, cast steel, etc.
	MA-3	95					1710	Can be used for refining stainless steel, military steel.
Siliceou*aterial	ZP-S				97.2		1650	Using acidic steel making, elting carbteel, low alloy steel, high silic*teel and ductile cast iron.
Magnesia Ramming	ZP-M1	91					1700	For all-capacity induction furnace, eltin*ganese steel, high alloy steel.
Magnesia Ramming	ZP-M2	97					1850	Vacuum induction furnace for *elting steel and high-temperature alloy precision.
Induction coil coating	ZP-T			85.3	4.7	4.6		Protective coating for the induction coil

内容声明：第一枪网为第三方互联网信息服务提供者，第一枪（含网站、微信、百家号等）所展示的产品/服务的标题、价格、详情等信息内容系由卖家发布，其真实性、准确性和合法性均由卖家负责，第一枪网概不负责，亦不负任何法律责任。第一枪网提醒您选择产品/服务前注意谨慎核实，如您对产品/服务的标题、价格、详情等任何信息有任何疑问的，请与卖家沟通确认；如您发现有任何违法/侵权信息，请立即向第一枪网举报并提供有效线索至b2b@dyq.cn

 